A new approach is reported for tailoring the pore geometry in five series of multivariate metal-organic frameworks (MOFs) based on the structure [Zn-2(bdc)(2)(dabco)] (bdc = 1,4-benzenedicarboxylate, dabco = 1,8-diazabicyclooctane), DMOF-1. A doping procedure has been adopted to form series of MOFs containing varying linker ratios. The series under investigation are [Zn-2(bdc)(2-x)(bdc-Br)(x)(dabco)]center dot nDMF 1 (bdc-Br = 2-bromo-1,4-benzenedicarboxylate), [Zn-2(bdc)(2-x)(bdc-I)(x)(dabco)]center dot nDMF 2 (bdc-I = 2-iodo-1,4-benzenedicarboxylate), [Zn-2(bdc)(2-x)(bdc-NO2)(x)(dabco)]center dot nDMF 3 (bdc-NO2 = 2-nitro-1,4-benzenedicarboxylate), [Zn-2(bdc)(2-x)(bdc-NH2)(x)(dabco)]center dot nDMF 4 (bdc-NH2 = 2-amino-1,4-benzenedicarboxylate) and [Zn-2(bdc-Br)(2-x)(bdc-I)(x)(dabco)] nDMF 5. Series 1-3 demonstrate a functionality-dependent pore geometry transition from the square, open pores of DMOF-1 to rhomboidal, narrow pores with increasing proportion of the 2-substituted bdc linker, with the rhomboidal-pore MOFs also showing a temperature-dependent phase change. In contrast, all members of series 4 and 5 have uniform pore geometries. In series 4 this is a square pore topology, whilst series 5 exhibits the rhomboidal pore form. Computational analyses reveal that the pore size and shape in systems 1 and 2 is altered through non-covalent interactions between the organic linkers within the framework, and that this can be controlled by the ligand functionality and ratio. This approach affords the potential to tailor pore geometry and shape within MOFs through judicious choice of ligand ratios.