Kennedy, N.; Holmes, J. D.; Long, B.
2020
November
Monolayer doping of germanium with arsenic: a new chemical route to achieve optimal dopant activation
Author
Published
1
()
Optional Fields
Raw data from: Langmuir 2020, 36, 9993.
Reported here is a new chemical route for the wet chemical functionalization of germanium (Ge), whereby arsanilic acid is covalently bound to a chlorine (Cl)-terminated surface. This new route is used to deliver high concentrations of arsenic (As) dopants to Ge, via monolayer doping (MLD). Doping, or the introduction of Group III or Group V impurity atoms into the crystal lattice of Group IV semiconductors, is essential to allow control over the electronic properties of the material to enable transistor devices to be switched on and off. MLD is a diffusion-based method for the introduction of these impurity atoms via surface-bound molecules, which offers a nondestructive alternative to ion implantation, the current industry doping standard, making it suitable for sub-10 nm structures. Ge, given its higher carrier mobilities, is a leading candidate to replace Si as the channel material in future devices. Combining the new chemical route with the existing MLD process yields active carrier concentrations of dopants (>1 1019 atoms/cm3) that rival those of ion implantation. It is shown that the dose of dopant delivered to Ge is also controllable by changing the size of the precursor molecule. X-ray photoelectron spectroscopy (XPS) data and density functional theory (DFT) calculations support the formation of a covalent bond between the arsanilic acid and the Cl-terminated Ge surface. Atomic force microscopy (AFM) indicates that the integrity of the surface is maintained throughout the chemical procedure, and electrochemical capacitance voltage (ECV) data shows a carrier concentration of 1.9 1019 atoms/cm3 corroborated by sheet resistance measurements.
Zenodo
https://doi.org/10.5281/zenodo.4195838
10.5281/zenodo.4195838
Grant Details